1580< Refractoriness< 1770
Long Time Materials
Refractory Material
Square, Circular, Triangular, etc
Mullite, Cordierite, High Alumina, etc
50*50, 40*40, 65*65, 50*75, etc
Product Description
Honeycomb Ceramic Filter are widely used in metallurgy and casting industry for the filter of melted metal. Usage of mullite/cordierite as its material and quality high density channel have endowed the products with good heat compression resistance and high casting temperature resistance, besides, flat channel design of honeycomb ceramic filter enable the balance between air flow rate and strength, and to remove the contaminants and cast particulates effectively, which hence improve the casting mechanic capability, surface look and product pass rate greatly.
Main advantages of honeycomb ceramic filter:
1.good work strength under high temperature, good thermal shock resistance and melted metal inflow resistance
2.high strength under room temperature, mechanic push resistance
3.obvious filter effect
4.ease the uneven inflow of casting, smooth the casting process, avoid surface defect
5.have a large and even melted inflow rate
6.good chemical stability, not affected by of melted meta, no change in its chemical compound
7.precise dimension and can be used in production line automatic filter mounting equipment
| Items | Parameters |
| Porosity(%) | 80~90 |
| Max. Operating Temperature(Degree C) | 1550 |
| Bulk Density (g/cm3) | 0.7~1.8 |
| Compression Strength(Mpa) | >15 |
| Thermal Shock Resistance(times/1100Degree C) | >6 |
| SiO2(%) | 38~42 |
| Al2O3(%) | 53~57 |
| Fe2O3(%) | <1.5 |
| TiO2(%) | <1.5 |
| Items | Parameters |
| Porosity(%) | 80~90 |
| Max. Operating Temperature(Degree C) | 1550 |
| Bulk Density (g/cm3) | 0.7~1.8 |
| Compression Strength(Mpa) | >15 |
| Thermal Shock Resistance(times/1100Degree C) | >6 |
| SiO2(%) | 38~42 |
| Al2O3(%) | 53~57 |
| Fe2O3(%) | <1.5 |
| TiO2(%) | <1.5 |
| Size (L×W mm) | Cell Shape | Cell Dia (mm) | No. of Cells | Porosity (%) | Pcs/Cubic Meter |
| 100×100×(20) | square | 2.2×2.2 | 33×33=1089 | 52.7 | 5000 |
| 100×100×(20) | square | 2.5×2.5 | 31×31=961 | 60.06 | 5000 |
| 100×100×(20) | square | 3.0×3.0 | 24×24=576 | 51.84 | 5000 |
| 81×81×(12.5) | square | 1.46×1.46 | 44×44=1936 | 62.89 | 12193 |
| 75×75×(15) | square | 2.2×2.2 | 26×26=676 | 58.17 | 11852 |
| 75×75×(15) | round | Φ2.5 | 492 | 42.94 | 11852 |
| 120×65x(20) | square | 2.2×2.2 | 38×20=760 | 47.16 | 6410 |
| 100×65×(20) | square | 2.2×2.2 | 33×21=693 | 51.6 | 7692 |
| 100×60(12.5) | square | 2.2×2.2 | 33×20=660 | 53.29 | 13333 |
| 100×50×(20) | square | 1.6×1.6 | 50×24=1200 | 61.44 | 10000 |
| 66×66×(12.5) | square | 1.2×1.2 | 42×42=1764 | 58.31 | 18365 |
| 66×66×(12.5) | square | 1.46×1.46 | 37×37=1369 | 66.99 | 18365 |
| 66×66×(12.5) | square | 2.2×2.2 | 26×26=676 | 75.11 | 18365 |
| 66×66×(12.5) | round | Φ2.4 | 440 | 45.7 | 18365 |
| 60×60×(20) | square | 1.6×1.6 | 29×29=841 | 59.8 | 13889 |
| 60×60×(15) | square | 2.2×2.2 | 20×20=400 | 53.78 | 18519 |
| 55×55×(12.5) | round | Φ2.3 | 367 | 50.41 | 26446 |
| 55×55×(12.5) | square | 2.2×2.2 | 21×21=441 | 70.56 | 26446 |
| 55×55×(12.5) | square | 1.15×1.15 | 37×37=1369 | 59.85 | 26446 |
| 50×50×(12) | square | 2.2×2.2 | 19×19=361 | 69.89 | 33333 |
| 50×50×(12.5) | round | Φ2.3 | 294 | 48.86 | 32000 |
| 40×40×(10) | round | Φ2.2 | 172 | 40.86 | 62500 |
| 40×40×(10) | square | 1.4×1.4 | 22×22=484 | 59.29 | 62500 |
| Φ90×(12.5) | square | 2.2×2.2 | 696 | 52.95 | 12582 |
| Φ60×(10) | square | 1.44×1.44 | 502 | 36.82 | 35368 |
| Φ52×(7) | square | 2×2 | 234 | 44.07 | 67304 |
| Φ52×(7) | square | 1.44×1.44 | 286 | 27.93 | 67304 |
| Φ50×(10) | round | Φ2.3 | 109 | 23.06 | 50955 |