Zirconia Ceramic Foam Filter for Zirconia Casting
Product Description
Zirconia cermic foam filter is applied to purge solution of carbon steel, steel alloy and stainless steel, it can endure require of technology of steel and get rid of foreign matter and materials of corroded model. Zirconia ceramic foam filter can also drop turulent and reduce twice oxided foreign matter. Zirconia ceramic foam filter is designed for the filtration of molten steel, alloy steel, and especially for high quality steel alloys casting temperature up to 1700 ° C, which have high porosity (76%-82%), high thremal shock resistance and large specific surface.
Technical Data:
Pore size (PPi): 10-60
Porosity (%): 80-90
Working temperature(° C): 1720
Bending Strength (Mpa): 0.8-1.0
Compression Strength (Mpa): 1.0-1.2
Thermal Shock Resistance(times/1100° C): 6
Advantages:
Ceramic foam filters help to enhanced quality of castings and reduce cost
*Special 3D structure to reduce turbulence of flowing molten metal
*Reduce defective rate of castings
*Improved mechanical properties of castings
*Improved precision of dimensions and shapes of castings
*Reduced costs of machining operations
*Simplify pouring systems and increase utilization ratio of mold
Technical Data:
Pore size (PPi): 10-60
Porosity (%): 80-90
Working temperature(° C): 1720
Bending Strength (Mpa): 0.8-1.0
Compression Strength (Mpa): 1.0-1.2
Thermal Shock Resistance(times/1100° C): 6
Advantages:
Ceramic foam filters help to enhanced quality of castings and reduce cost
*Special 3D structure to reduce turbulence of flowing molten metal
*Reduce defective rate of castings
*Improved mechanical properties of castings
*Improved precision of dimensions and shapes of castings
*Reduced costs of machining operations
*Simplify pouring systems and increase utilization ratio of mold
| Color | Yellow | PPI | 10-60 |
| Porosity (%) | 70~80 | Filtration capacity (kg/cm⊃2;) | ≥2.5 |
| Bulk density (g/cm⊃3;) | 0.9~1.1 | Temperature (celsius degree) | ≤1700 |
| Compressive strength (Mpa) | ≥1.75 | Heat shock | Excellent |
| Materials | Zirconia |
| Working Temp. ( ° C) | ≤ 1700 |
| Color | Yellow |
| Pore Size ( PPI ) | 10 |
| Porosity ( % ) | 76~82 |
| Compression Strength ( MPa ) | ≥ 2.5 |
| Bulk Density ( g/cm 3 ) | 0.7~1.1 |
| Thermal Shock Resistance | Excellent |
| Application | Carbon steel low alloy steel |
| Dimensions mm | Flow rate(kg/s) | Total capacity | |
| Carbon steel | High-alloy steel | kg | |
| 40 × 40 × 20 | 2 | 2.5 | 30 |
| 50 × 50 × 22 | 3 | 4 | 50 |
| 55 × 55 × 22 | 4 | 5 | 60 |
| Φ 50 × 22 | 2.5 | 3 | 40 |
| Φ 60 × 25 | 3.5 | 4.5 | 70 |
| Φ 70 × 25 | 4.5 | 6 | 95 |
| Φ 75 × 25 | 5 | 6.5 | 110 |
| Φ 80 × 25 | 6 | 7.5 | 125 |
| Φ 90 × 25 | 8 | 9.5 | 160 |
| Φ 100 × 25 | 9.5 | 12 | 190 |
| Φ 120 × 25 | 11 | 14 | 220 |
| Φ 150 × 30 | 12.5 | 15 | 330 |